WELDING ELECTRODE

Rutile coated stick electrode for welding corrosion-resistant steels. Weld metal comprises austenitic stainless steel 18/8 Cr/Ni, AISI 301, 302, 304

Rutile coated stick electrode for welding corrosion-resistant steels. Weld metal comprises austenitic chrome nickel molybdenum steel with extremely low carbon content for operating temperature up to 350°C. Tensile strength : 650 N/mm²  elongation : 35%

Rutile coated stick electrode for welding heat-resistant steels. Weld metal comprises fully austenitic chrome nickel steel, scale-resistant up to 1200°C.
Tensile strength : 600 N/mm²  elongation : 35%

Rutile coated high-output electrode with 160% deposit rate for joint welding dissimilar steels and for hardfacings on rails, switch point, dredger teeth, baffleplates. Weld metal comprises austenitic chrome nickel manganese steel, scale-resistant up to 850°C; work-hardening. Tensile strength : 650 N/mm²  elongation : 35%

Rutile coated stick electrode for welding dissimilar steels and for hard-facings. Weld metal comprises austenitic chrome nickel steel with increased ferrite content: scale resistant up to 1000°C; wear- resistant; corrosion-resistant; heat-resistant.
Tensile strength : 650 N/mm²  elongation : 20%

Basic graphitic coated stick electrode with pure nickel core wire for machinable cold welds on cast iron. Brinell hardness approx. 150.

Basic graphitic coated stick electrode with nickel iron core wire (b-metal) for machinable cold welds on cast iron, spheroidal graphite iron and in combination with steel.

For rebuilding of small miscastings and repair welding of sand holes in FC and FCD qualities by cast iron welding. 

Basic coated stick electrode for machinable, wear resistant hardfacing. Weld metal comprises low-alloyed manganese chromium steel. Easy slag removal. Preheat parent materials which are susceptible to cracking to approx. 250°C.

Rutile coated high-output electrode with 180% deposit rate for tough, abrasion-resistant hardfacing on machine components made from structural steel, steel casting or austenitic manganese steel.
Preheat parent materials which are highly carburized of susceptible to cracking to approx. 200° to 300°C.
Vickers hardness 650; Rockwell hardness 58.
Untreated weld metal only can be machined by grinding.

Rutile coated high-output electrode with 170% recovery for welding very hard, extremely wear-resistant hardfacings which are subjected to very high abrasive wear through sand, gravel, ore, coal, cement or other abrasive materials.
Vickers hardness 650; Rockwell hardness 58.
Weld metal can only be machined by grinding.

Basic graphitic coated stick electrode for welding extremely wear-resistant hardfacings. High weld deposit rate of 170%. Weld metal comprises chromium hard-alloy.

Basic graphitic coated high-output electrode with 240% deposit rate for welding extremely wear-resistant special carbide hardfacings on components which are subjected to severe abrasive wear though sand, gravel, ore, coal, cement, slag.
Vickers hardness 820; Rockwell hardness 65.
Weld metal machinable only by grinding.