Corodur® 300
MF 1-300-P

A low-alloyed flux-cored wire electrode for building up applications that can be used for multi- layer welding because the weld metal is crack-free and ductile. Deposits are machinable. Used primarily on tractor wheels, steel shafts, gear and trunion rail links.

Corodur® 600 TIC
MF-6-60-GP

C-, Cr-, Ti- and Mo-alloyed flux-cored wire electrode for parts that are exposed to high abrasive wear in combination with impact stress. The micro structure of the deposit is martensitic with inserted Titanium - carbides. Applications are cement crusher rolls, pulveriser rolls and hammers.

Corodur® 450
MF 5-45-PT

Corodur 450 is a tubular wire that produces a low alloyed deposit for hardfacing of approximately 450 HB. Deposits are machinable. This electrode can be used for multi-layer welding. Applications are wheel rims, chain links, bucket chains. For base materials with higher carbon content, a buffer layer or pre-heating may be needed.

Corodur® 601
MF 6-60-PT

C-, Cr-, Mo-, W-, V- alloyed weld deposit with excellent properties of resistance to abrasion and impact. The deposit has a high hot hardness up to 550° C. Deposits can be heat treated to increase the hardness. For use on hammer and blooming table rolls, crusher bars and bucket teeth.

Corodur® 612
MF 6-55-RP

High Cr-alloyed (12,5% Cr) flux-cored wire electrode for welding wear resistant layers with a martensitic micro structure. The welding deposit is resistant against corrosion, cavitation and high compressive load (metal to metal) up to 500° C. Typical applications are leading rolls, armatures, liquid and sand pumps.