Corodur® 42 MIG
MF 10-45-CGT

C-, Cr-, Ni-, Mo-alloyed flux-cored wire electrode for hardfacing on parts that are exposed to abrasive wear in combination with medium impact stress. The weld deposit is corrosion resistant
and machinable. Typical applications are found in the chemical and food industry.

Corodur® 59
MF 10-60-GR

C-, Cr-alloyed flux-cored wire electrode that deposits a high chrome carbide weld metal with excellent resistance to abrasion and moderate impact. Deposits are not machinable. For higher corrosion resistance available as CORODUR 59L.

Corodur® 55 Mo
MF 10-60-G

C-, Cr-, Mo-alloyed flux-cored wire electrode for hardfacing on parts that are exposed to high abrasive mineral wear. In comparison to Corodur 55, the weld deposit of this electrode has a higher temperature resistance (up to 450°C). Used for pumps, mixer parts and conveyer screws.

Corodur® 60
MF 10-60-G

High C-, Cr-, Nb-alloyed flux-cored wire electrode for high abrasive wear up to 450°C. The weld deposit consists of chrome- and niobium-carbides. Weld metal is not machinable. Maximum deposit should be limited to three layers. For mixers, Ni-hard cones and tables, wear plates.

Corodur® 61
MF 10-65-G

High C-, Cr-, Nb-, B-alloyed flux-cored wire electrode with special carbides in extreme hardness. This combination results in high
abrasion resistance. Applications are found in the hardfacing of
mining equipment, augers, impellers, dredgers and wear plates.

Corodur® 68
MF 10-70-GCZ

Very high C-, Cr-, B-alloyed flux-cored wire electrode for extreme hard and non-corrosive hardfacing against very high mineral wear also at high temperatures. The weld deposit has a ledeburitic structure, bearing many various hyper-
eutectic carbides. A maximum deposit thickness of 6 mm
(1-2 layers) is recommended.
Hardness Reduction at 400°C app. 5%, at 600°C app. 10%.

Corodur® 64
MF 10-64-GZ

C-, Cr-, B-, W-, V-alloyed flux-cored wire electrode that deposits a very hard martensitic micro structure with carbides. The deposit is resistant against heavy mineral abrasion at higher temperatures.

This wire can be used for one layer welding without loss of hardness. For mineral and brick industry screws and van - blades. Hardness reduction at 400°C app. 15%, at 600°C app. 25%.

Corodur® 78
MF 10-70-GZ

C-, Cr-, V-, Nb-alloyed flux-cored wire electrode for extreme mineral wear. The weld deposit has a high scratch hardness. Applications are sinter plants, lignite mining machines, gravel industry, chains, etc.
Hardness Reduction at 400°C app 7%.

Corodur® 65
MF 10-65-GZ

High C-, Cr-, Mo-, Nb-, V-, W-alloyed flux-cored wire electrode, which forms extremely hard carbides. This is used for hardfacing against extremely heavy mineral wear. The deposit retains
its wear resistance up to 650°C. This wire is recommended for use in sintering plants, augers and blast furnace bells.

Hardness reduction at 400°C app. 4%, at 650°C app. 10%.